Consolidated Refractories Australasia Pty. Ltd Insulating Fire Brick

Homepage Homepage
Enquiries Enquiries
Refractory Plastics & Ramming Refractory Plastics & Ramming
Insulating Fire Brick Insulating Fire Brick
Dense Fire Brick Dense Fire Brick
Ceramic Fire Blanket Ceramic Fibre Blanket
Castables Castables
Mortars Mortars
Insulating Board Insulating Board
Thermobond & Phoscrete Thermobond & Phoscrete
Coatings Coatings
Glass Accessories Glass Accessories
Miscellaneous Miscellaneous
Specialist Shapes Specialist Shapes

Insulating Fire BrickConsolidated Refractories supply a wide selection of insulating firebrick. As agent for ISOLITE Singapore we stock the isolite range of quality Insulating Firebricks. We are also supply other quality brick on request.

We supply Insulating brick into the following areas :

  • Kilns
  • Heat treatment Furnaces
  • Crucible Furnace
  • Cremators
  • Glass and Frit Furnaces
  • Waste Recovery
  • Incinerators
  • Combustion Chamgers
  • Brick Kilns
  • Boilers
Tech Data
Tech data sheet details for B5/R123, B6/R126, B7/R128, LKB23, LKB26, LKB28

Properties/Products B5 B6 B7 LBK
237
LBK
26
LBK
28

Classification Temp °C 1200 1300 1400 1500 1300 1400
°F        2200 2400 2600 2800 2400 2600
Bulk Density g/cm 2 0.78 0.78 0.87 0.96 1.06 1.16
Thermal Conductivity
W/mk (kcal/mh°c)
0.24
(0.21)
0.26
(0.22)
0.28
(0.24)
0.34
(0.29)
0.33
(0.28)
0.42
(0.36)
Reheat Shrinkage
% at ( ) °C x 8 hrs
0.0
(1200)
0.50
(1300)
0.60
(1400)
0.90
(1500)
0.30
(1300)
0.90
(1400)
Cold Curshing Strength
MPa
(kg/cm2)
2.7
(28)
2.7
(28)
3.2
(33)
3.6
(37)
6.1
(63)
7.6
(78)
Modulus of Rupture
MPa
(kg/cm2)
2.3
(23)
1.7
(17)
2.0
(20)
2.0
(20)
2.5
(25)
3.1
(32)
Thermal Expansion
% at .( ) °C
0.50
(1000)
0.50
(1000)
0.48
(1000)
0.50
(1000)
0.50
(1000)
0.51
(1000)
Chemical Composition
AI2O3
SiO2
Fe2O3
CaO

40
55
1.3
0.4

40
55
1.3
0.4

41
54
1.4
0.2

68
30
0.9
0.8

40
56
1.3
0.3

41
55
1.2
0.4
Recommended
ISOLITE Mortar
SAS-D HAS-D SAS-D HAS-D

<< Back^ TopHomepage © Copyright Consolidated Refractories Australasia Pty. Ltd 2000